Narrow bandgap quantum dot diode structures and photoresistors for thermo-photovoltaic and infrared applications 

Karen M. Gambaryan* 

Department of Physics of Semiconductors and Microelectronics, Yerevan State University, 0025, Armenia 

Adv. Mater. Lett., 2018, 9 (2), pp 112-115

DOI: 10.5185/amlett.2018.1804

Publication Date (Web): May 16, 2018

E-mail: kgambaryan@ysu.am

Abstract


For the thermophotovoltaic (TPV) and other mid-infrared applications, the narrow bandgap quantum dot (QD) diode structures and photoresistors (PR) based on InAsSbP alloys and InAs industrial substrates are fabricated and investigated. For the nucleation of InAsSbP composition strain-induced QDs in Stranski–Krastanow growth mode, as well as at the growth of emitter epilayer lattice-matched with the InAs(100) substrate, the modified liquid phase epitaxy (MLPE) technique is employed. The HR-SEM and AFM microscopes are used for characterization. The grown QDs surface density equals to (3-8)×109 cm-2, with height and width dimensions ranges from 4 nm to 15 nm and 10 nm to 35 nm, respectively. The current-voltage characteristics and photoresponse spectra of QD TPV and PR structures are also explored. The redshift of the absorption edge, as well as enlargement toward the short wavelength region is revealed for both QD-based devices. The quantitative calculations show increasing of QD-based TPV structures efficiency up to 16% compared with the same structures without QDs. 

Keywords

TPV, quantum dots, diode heterostructures, photoresistors, mid-infrared.