Ce3+ and Eu3+ activtated Na2Sr2Al2PO4F9 nanophosphor

Ce3+ and Eu3+ activtated Na2Sr2Al2PO4F9 nanophosphor

S. J. Dhoble*, K. N. Shinde

Department of Physics, RTM Nagpur University, Nagpur 440033, India

Adv. Mater. Lett., 2011, 2 (5), pp 349-353

DOI: 10.5185/amlett.2011.3072am2011

Publication Date (Web): Apr 08, 2012

E-mail: sjdhoble@rediffmail.com


A halophosphate based nanophosphor has been synthesized by wet chemical method. XRD confirms the preparation of nanophosphor and this article presents the luminescence properties of Ce3+ and Eu3+ activated Na2Sr2Al2PO4F9 under UV/NUV excitation. The photoluminescence spectrum comprises of a main peak in the range 270–350 nm with a shoulder in the range 350–370 nm, which may be ascribed to transitions from 5d–4f levels of cerium in the mixed host lattice (Na2Sr2Al2PO4F9). In Na2Sr2Al2PO4F9: Eu3+ nanophosphor, orange/red luminescence under the near ultraviolet excitation of 393 nm, attributed to the transitions from 5D0 excited states to 7FJ (J=0–4) ground states of Eu3+ ions.


Nanophosphors, wet chemical synthesis, white lighting, photoluminescence

Upcoming Congress

Knowledge Experience at Sea TM