Zinc oxide; hexagonal microprisms; nanostructure.

One-pot Reaction To Synthesis And Characterization Of Two-stage Zinc Oxide Hexagonal Microprism On Nickel Thin Films

Wei Wu1*, Shaofeng Zhang2,3, Xiangheng Xiao2,3, Changzhong Jiang2,3*

1School of Printing and Packaging and School of Chemistry and Molecular Science,

2Key Laboratory of Artificial Micro- and Nano-structures of Ministry of Education,

3Center for Electronic Microscopy and School of Physics and Technology, Wuhan University, Wuhan 430072, P. R. China

Adv. Mater. Lett., 2013, Current Issue, 4 (8), pp 610-614

DOI: 10.5185/amlett.2012.12477

Publication Date (Web): Jul 13, 2013

E-mail: weiwu@whu.edu.cn, czjiang@whu.edu.cn


A novel two-stage zinc oxide (ZnO) hexagonal microprisms was successfully synthesis via a hydrothermal route on a nickel (Ni) thin films. The Ni thin films are deposited by using magnetron sputtering onto Si (100) substrate. The formation of the secondary structure and optical properties of ZnO microprism have been investigated and the formation mechanism has been discussed. The results illustrate the Ni substrate is a key factor to grow the two-stage ZnO, and the photoluminescence (PL) emission peak at 389 nm reveals that the high crystal quality of these nanorods. ZnO with its excellent luminescent properties and the controllable nanostructures will hold promise for the development of photonic devices.