Swift heavy ion induced modifications in the structural, optical and methane sensing properties of indium oxide thin films - A comparative study using Ag9+ and O7+ ion irradiation

Riti Sethi1, Anver Aziz1, G.B.V.S. Lakshmi2, D.K. Avasthi3 , Azher M. Siddiqui1*

1Department of Physics, Jamia Millia Islamia, New Delhi 110025, India

2Special Center for Nanosciences, Jawaharlal Nehru University, New Delhi 110067, India

3Amity Institute of Nanotechnology, Noida, Uttar Pradesh 201313, India

Adv. Mater. Lett., 2018, 9 (7), pp 481-487

DOI: 10.5185/amlett.2018.2033

Publication Date (Web): Jun 14, 2018

E-mail: amsiddiqui@jmi.ac.in

Abstract


Thin films of indium oxide grown on quartz substrates were subjected to 100 MeV Ag9+ and O7+ ions irradiation. The pristine and swift heavy ions irradiated films were characterized using X-ray Diffraction, Rutherford Backscattering Spectrometry, Scanning Electron Microscopy and UV-Vis Spectroscopy to examine the effect of irradiation with ions having large difference in the values of electronic energy loss (Se) on the structural, microstructural and optical properties of indium oxide thin films. XRD and SEM studies revealed deterioration in crystallinity along with decrease in both crystallite size and grain size upon irradiation with both Ag9+ and O7+ ions. However, the decrease in the crystallite size and grain size in comparison to the pristine film was more radical for irradiation with Ag9+ ions. RBS spectra suggest that the electronic sputtering in the indium oxide films due to SHI irradiation is very less. AFM images illustrate the decrease in surface roughness from 29.8 nm for the pristine film to to 27.4 nm and 26.7 nm on irradiation with 100 MeV O7+ and Ag9+ ions at a fluence of 3.3×1013 ions/cm2.  Also, UV-Vis study revealed an increment in the value of optical band gap from 3.41 eV for the pristine film to 3.53 and 3.67 eV for indium oxide films irradiated with of 3.3×1013 ions/cm2 fluence of O7+ and Ag9+ ions respectively. The irradiation induced structural and optical modifications have been explained using the Thermal spike model. Along with the structural and optical properties, sensing properties of the pristine and irradiated films for 100 ppm methane gas at an operating temperature of 300oC have also been examined and the results have been correlated with the induced structural modifications.

Keywords

Indium oxide, swift heavy ions, electronic energy loss, thermal spike, gas sensing.

Current Issue
The Journey of a Decade to Advancing Materials
Are the Electrospun Polymers Polymeric Fibers?
Mechanical and Thermal Properties of Composite Material and Insulation for a Single Walled Tank for Cryogenic Liquids
Prediction of Long-Term Behavior for Dynamically Loaded TPU
Investigation of Doped Titanium Dioxide in Anatase Phase. Study ab initio using Density Functional Theory
Comparison between Single Al2O3 or HfO2 Single Dielectric Layers and their Nanolaminated Systems
Preparation of Stable and Optimized Antibody-gold Nanoparticle Conjugates for Point of Care Test Immunoassays
Resonance-Based Temperature Sensors using a Wafer Level Vacuum Packaged SOI MEMS Process
Integrated System Based on the Hall Sensors Incorporating Compensation of the Distortions
The Efficacy of Cinnamomum Tamala as a Potential Antimicrobial Substance against the Multi-Drug Resistant Enterococcus Faecalis from Clinical Isolates
The Effect of Complexing Reagent on Structural, Electrical and Optical Properties of CuS Thin Film
Laser Cladding of Fluorapatite Nanopowders on Ti6Al4V
Preparation and Evaluation of Sulfonate Polyethylene Glycol Borate Ester as a Modifier of Functional Properties of Complex Petroleum Lithium Grease

Upcoming Congress

Knowledge Experience at Sea TM