Determination of optimum cation to anion (Cd:S) ratio for the synthesis of mono sized CdS quantum dots through optical properties

Jai Kumar B, Sumanth Kumar D, Mahesh H. M* 

Thin film solar cell lab., Department of Electronic Science, Bangalore University, Bangaluru, 560056, India

Adv. Mater. Lett., 2017, 8 (4), pp 386-392

DOI: 10.5185/amlett.2017.6918

Publication Date (Web): Mar 14, 2017

E-mail: hm_mahesh@rediffmail.com

Abstract


The CdS quantum dots (QDs) were synthesized using double injection aqueous method and systematic studies were carried to determine optimum cation to anion (Cd:S) ratio to obtain mono sized CdS QDs. An efficient and convenient method is designed by utilizing the optical properties (absorbance and transmission spectra) as qualitative tool. CdS QDs was synthesized by varying cadmium and sulfur concentration from 0.01M to 0.1M and 0.01M to 0.05M respectively keeping MPA and other precursors constant. Through Concentration Optimization by Optical Spectra (COOS) method, it was found that for 0.02M sulfur and 0.04M MPA, 0.03 to 0.05M cadmium was the most favorable concentration and similarly for 0.04M cadmium and MPA the optimum concentration of sulfur was 0.02M. CdS QDs optical band gap varied from 3.09 eV to 3.69 eV with quantum dots size decreasing from 3.22 nm to 2.45 nm, respectively for Cadmium concentration from 0.02M to 0.07M. For Sulfur concentration variation, band gap varied from 3.55 eV to 3.03 eV, with size of QDs increasing from 2.58 nm to 3.33 nm, respectively for concentration 0.01M to 0.05M. All this results shows that synthesized quantum dots were well under quantum confinement effect. Further, the proposed COOS method can be extended to all QDs synthesis to obtain the optimum cation to anion ratio to synthesis QDs with narrow size distribution.

Keywords

CdS, quantum dots, MPA, concentration optimization by optical spectra (COOS) method, Cd:S ratio concentration study, optical properties.

Previous issues

Celebrating 10th Years of Diamond Open Access Publishing in Advanced Materials  

Cerebral Oxygenation Studies Through Near Infrared Spectroscopy: A Review

Analysis of Fine Sulfoaluminate Cement by Strength and Thermogravimetric Analysis

Characterization of the Interfacial Surface Energy for Composite Electrical Conduction Measurements using Two Full Range Percolation Threshold Models

Quantitative Detect of Fatigue of Membrane of Erythrocyte in Uniform Shear Field

Ecofriendly-developed Polyacrylic Acid-coated Magnetic Nanoparticles as Catalysts in Photo-fenton Processes

Evaluation of Drug Interactions with Medications Prescribed to Ambulatory Patients with Metabolic Syndrome in Urban Area

Fiber-reinforced Cementitious Composite: Sensitivity Analysis and Parameter Identification 

Evaluation of Drug Utilization Patterns Based on World Health Organization Drug use Indicators at Outpatients Clinics

Are Quantitatively Micro-machined Scaffolds Effective for Cell Technology?

Synthesis and Characterization of Gold Nanoparticles from Lobelia Nicotianifolia Leaf Extract and its Biological Activities

Advanced Oxidations of Tartrazine Azo-dye

Antifungal Activity of Salvia jordanii Against the Oral Thrush Caused by the Cosmopolitan Yeast Candida albicans among Elderly Diabetic Type 2 patients

Upcoming Congress

Knowledge Experience at Sea TM