FT-IR study of Cu substituted Ni-Zn ferrites prepared by citrate precursor method
Biju Thangjam, Ibetombi Soibam
Volume 2, Issue 3, Page 205-208, Year 2017 | DOI: 10.5185/amp.2017/3014
Keywords: Ferrites, citrate precursor method, FT-IR, force constants, Jahn-Teller effect.
Abstract: Ni-Cu-Zn ferrites with compositional formula Ni0.8-xCuxZn0.2Fe2O4, where 0.0≤x≤0.5 in steps of 0.1 were synthesized by the citrate precursor method. The samples were subjected to final sintering at 900?C for 2h after a pre-sintering at 600?C for 4h. X-ray diffraction patterns confirmed the formation of single phase spinel structure. The average crystallite size was calculated using Scherrer’s formula and was found to vary from 33nm to 39nm, clearly indicating the formation of nanoparticles. The infrared spectra were recorded at room temperature for all the samples in the range of 450 cm‾1 to 4000 cm‾1 using Perkin Elmer FT-IR Spectrometer. Jahn-Teller effect emerges which can be identified through the FT-IR Spectroscopy of the samples. This phenomenon may result in useful electro and magneto- optical applications. Possible mechanism is being discussed. Copyright © 2017 VBRI Press.