Thickness Modulated Structural And Photo-luminescence Properties Of Magnetron Sputtered Nanocrystalline SiC Ultrathin Films

Narendra Singh and Davinder Kaur

Volume 2, Issue 11, Page 725-728, Year 2017 | DOI: 10.5185/amp.2017/782

Keywords: Thin films, sputtering, XRD, XRR, photoluminescence.

Abstract: Ultrathin silicon carbide (SiC) films were grown on p type Si (100) substrate by RF magnetron sputtering at constant substrate temperature of 7000C for investigating thickness dependence of structural and photoluminescence properties. The structural and Photoluminescence properties were measured by X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR) and photospectrometer respectively. X-ray diffraction pattern revealed (102) and dominant (105) reflections which corresponds to 4H-SiC and an enhancement in (105) peak intensity with increasing thickness was also observed. The thickness measured by X-ray reflectometry (XRR) reduces from ~ 46 nm to 12 nm by decreasing deposition time (40-10 minute) which in turn reduces the crystallite size. Photoluminescence spectra show a broad peak extending from ultraviolet to blue region centered at ~ 385 nm for film of thickness ~ 46 nm (deposition time 40 min). A shifting in Photoluminescence peak towards shorter wavelength (blue shift) with decreasing SiC ultrathin film thickness was observed, which could be attributed to quantum confinement effect. The improved Photoluminescence in ultrathin nanocrystalline SiC films could make it a potential candidate in optoelectronic and biomedical applications. Copyright © 2017 VBRI Press.

Advanced Materials Proceedings

The official journal of the International Association of Advanced Materials (IAAM)